세우씨앤이 > 제품소개 1 페이지

무제 문서

- Grinding Media

Zirconia Beads.jpg

지르코니아 비드

Yittria Stabilized Zirconia Bead

Standard Size of Beads

0.03mm*,

0.05mm* ,

0.1mm ,

0.2mm ,

0.3mm ,

0.4mm ,

0.5mm

0.65mm ,

0.8mm ,

1.0mm ,

1.25mm ,

1.5mm

1.75mm ,

2.0mm ,

2.35mm ,

2.5mm

3.0mm ,

4.0mm ,

5.0mm ,

10mm

Material	Composition ratio(wt%)
ZrO₂ (+HfO₂)	94.75±0.60
Y₂O₃	4.90±0.50
Al₂O₃	0.30±0.10
Fe₂O₃	0.01
SiO₂	0.01
TiO₂	0.01
Na₂O	0.01
MgO	0.01

Physical Properties

Density(g/cm³)	6.0
Microhardness(Vickers hardness : Hv)	1150-1200
Young's Modulus (GPa)	210-220
Moduluds of Rapture(MPa)	1000
Average Grain Size(μm)	0.3-0.4